Zinc wire for thermal spray application
- Ing Enrico Conte
- Topic Author
- Offline
- Fresh Boarder
-
Less More
9 years 5 days ago #2924 by Ing Enrico Conte
Zinc wire for thermal spray application was created by Ing Enrico Conte
Hello everybody !!
For wiredrawing zinc wire (EN-ISO 14919, inlet dia.4-4,5mm, min.outlet dia.1,2-1,6mm) which is the best elongation for the die sequence ? I was thinking that an elongation 19-21% could be ok in a fully submerged machine.
What do you think ? Any suggestion ?
For wiredrawing zinc wire (EN-ISO 14919, inlet dia.4-4,5mm, min.outlet dia.1,2-1,6mm) which is the best elongation for the die sequence ? I was thinking that an elongation 19-21% could be ok in a fully submerged machine.
What do you think ? Any suggestion ?
Please Log in to join the conversation.
- Peter J Stewart-Hay
- Offline
- Moderator
-
Less More
- Posts: 126
- Thank you received: 21
8 years 11 months ago #2929 by Peter J Stewart-Hay
Regards,
Peter J. Stewart-Hay Principal
Stewart-Hay Associates
www.Stewart-Hay.com
This email address is being protected from spambots. You need JavaScript enabled to view it.
Replied by Peter J Stewart-Hay on topic Zinc wire for thermal spray application
Hello Enrico,
I have checked all my reference books, all over the Internet and used the WAI Education Abstract Search but I can find no information on drawing zinc wire from rod or larger diameter wire. It may therefore take a longer period of time to get an answer because we are dependent upon a qualified reader to provide the appropriate information. I think a fully submerged machine would be the right approach but as far as the elongation goes, it is definitely a question. Sorry I cannot help further.
I have checked all my reference books, all over the Internet and used the WAI Education Abstract Search but I can find no information on drawing zinc wire from rod or larger diameter wire. It may therefore take a longer period of time to get an answer because we are dependent upon a qualified reader to provide the appropriate information. I think a fully submerged machine would be the right approach but as far as the elongation goes, it is definitely a question. Sorry I cannot help further.
Regards,
Peter J. Stewart-Hay Principal
Stewart-Hay Associates
www.Stewart-Hay.com
This email address is being protected from spambots. You need JavaScript enabled to view it.
Please Log in to join the conversation.
- Ing Enrico Conte
- Topic Author
- Offline
- Fresh Boarder
-
Less More
- Posts: 8
- Thank you received: 0
8 years 11 months ago #2930 by Ing Enrico Conte
Replied by Ing Enrico Conte on topic Zinc wire for thermal spray application
Hi Peter, thanks for your reply.
I've searched some info on internet, but I didn't find any particularly info apart general info about characteristics of zinc etc.
I will share all info I'll get in next weeks with all of you.
Enrico
I've searched some info on internet, but I didn't find any particularly info apart general info about characteristics of zinc etc.
I will share all info I'll get in next weeks with all of you.
Enrico
Please Log in to join the conversation.