Using a .105 diameter 1065 carbon steel as a process size, what would be the thickness in oz/ft2 of a hot dip galvanized coating? Also, if this .105 wire were drawn down to .050", what would be the calculated thickness of the coating at that size? Thanks for any help. Mike Caranna
Please Log in to join the conversation.
- Archived Forum Admin
- Topic Author
- Offline
- Platnium Boarder
-
12 years 11 months ago #1214 by Archived Forum Admin
Replied by Archived Forum Admin on topic Re: Hot dip galvanizing
I would recommend that you send an email to Mack Young at Davis Wire. He is an expert in that field and I'm sure he would be happy to answer your question.
This email address is being protected from spambots. You need JavaScript enabled to view it.
This email address is being protected from spambots. You need JavaScript enabled to view it.
Please Log in to join the conversation.
- Archived Forum Admin
- Topic Author
- Offline
- Platnium Boarder
-
12 years 11 months ago #1215 by Archived Forum Admin
Replied by Archived Forum Admin on topic Re: Hot dip galvanizing
The Galvanizing temperature ( Zic Bath temperature ) and time of inmersion ( lenght of inmersion / speed )are variables affecting the coating.
In general, these are the coatings that should be expected on 1065 steel:
.105" 1.2 oz/ ft2
.050" 0.5 oz/ ft2
Kindest Regards
Eduardo Anaya
In general, these are the coatings that should be expected on 1065 steel:
.105" 1.2 oz/ ft2
.050" 0.5 oz/ ft2
Kindest Regards
Eduardo Anaya
Please Log in to join the conversation.
- Archived Forum Admin
- Topic Author
- Offline
- Platnium Boarder
-
12 years 11 months ago #1216 by Archived Forum Admin
Replied by Archived Forum Admin on topic Re: Hot dip galvanizing
The method of wiping the molten zinc is the primary determiner.
Firstadams
Firstadams
Please Log in to join the conversation.